Tin cure silicone T-Brush series

Brushable Silicone, self-thickens for making fast brush-on molds of almost any model.

4 thin layers is all that is necessary to make a strong and durable production mold for casting wax, gypsum, concrete or resins.

Vacuum degassing mixed material using a vacuum pump and chamber to remove entrapped air is recommended.

Sculpture and statues mold making rubber

Features

  • Brushable application
  • High tear strength
  • High elasticity, for easy removal of, complex replica parts
  • Less shrinkage
  • Outstanding release properties
Sculpture, Foundry & Figurines

Typical Uses & Casting Materials

These rubbers are commonly used in Sculpture, Architectural Reproduction & Restoration applications.

It is used to make rubber molds that can be used to cast polyurethanes, epoxy’s, polyester’s, cement, concrete, soap, wax, plaster, etc..

Instruction

  1. Stir Part A well before use, shake Part B catalyst container well before use.
  2. Weigh 100 Part A to 2~3 Part B using an accurate scale and a clean mixing container.
  3. Vigorously mix and scrape walls of the container, continue mixing until uniform.
  4. Place the mixture in a vacuum chamber & degass. If without a chamber, Pour the mixture 2-3 inches above the pattern in a thin stream.
  5. Allow the silicone to cure 2-4 hours and demold with care.

Important tips

  • Before use, read the operation manual, please.
  • Before large production, a small-scale test is recommended.
  • Mixing ratio must be accurate, recommend mixing ratio is A:B=100:2~3(by weight), If curing too fast, please reduce the ratio of catalyst to 1% or less, then Stir Part A and Part B completely.
  • Use a vacuum to de-gas this product before use under pressure. Vacuum silicone for 2-3 minutes
  • This product has a limited shelf life. Use it as soon as possible after opening.
  • Always tightly reseal containers after use. Air, moisture or other contamination causes a reduction in reactivity over time.

Package

Storage & shelf-life

12 months in unopened containers when properly stored.

Super-Silicon cannot guarantee the shelf life of opened or repackaged units.
Recommended storage temperature range: 10°C – 25°C. SuperSilicon™ should be stored in closed containers out of direct sunlight and away from direct sources of heat. Always tightly reseal containers after use. Air, moisture or other contamination causes a reduction in reactivity over time.

ProductsDescription
Thickening agentFor Thickening silicone for brushable application
Fumed silicaA fine powder that can be added to polyurethane and silicone liquid rubber to thicken them for brush-on/lay-up applications.
Tin Cure Silicone AcceleratorFor speed up curing time
Heat resistance additiveFor resisting chemical/heat burnout
Pigments For coloring silicone
FabricReinforcement Material for silicone molds
Release agent

Contacts
Get a Free Sample, Contact Us Now
Scroll to Top